Transport properties and microstructure of mono- and seven-core wires of FeSe1-xTex superconductor by Fe-diffusion powder-in-tube method
Toshinori Ozaki, Keita Deguchi, Yoshikazu Mizuguchi, Yasuna Kawasaki, Takayoshi Tanaka, Takahide Yamaguchi, Shunsuke Tsuda, Hiroaki Kumakura, Yoshihiko Takano
arXiv:1103.0402 · DOI 10.1088/0953-2048/24/10/105002 · 2011-03-02 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report the successful fabrication of mono- and seven-core superconducting wires of FeSe1-xTex using an in-situ Fe-diffusion process based on the powder-in-tube (Fe-diffusion PIT) method. The reacted layer in these wires were found to have composite structure with composition nearly FeSe and FeTe for the inner and outer layers, although a single layer of composition FeSe0.5Te0.5 was supposed to be formed. The self-field transport Jc values at 4.2 K were found to be 226.2 A/cm2 and 100.3 A/cm2 respectively for mono- and seven-core wires. The Jc's of mono- and seven-core wires dropped rapidly at low fields and then showed a gradual decrease with increasing magnetic fields. In addition, the seven-core wire showed higher Jc than the mono-core wire under higher magnetic fields, indicating that the seven-core wire of FeSe1-xTex superconductor using Fe-diffusion PIT method is advantageous for the superconducting-wire application under high magnetic fields.
Similar papers
Fabrication of binary FeSe superconducting wires by novel diffusion process
similarity 0.96Toshinori Ozaki et al. · 2011 · arXiv:1103.3602
Source status unknown — claims are unverified
Microstructure and transport properties of FeTe0.5Se0.5 superconducting wires fabricated by ex-situ Powder-in-tube process
similarity 0.93T. Ozaki et al. · 2010 · arXiv:1012.1404
Source status unknown — claims are unverified
Transport properties of the single- and 3-core Fe-Se wires fabricated by a novel chemical-transformation PIT process
similarity 0.93Yoshikazu Mizuguchi et al. · 2011 · arXiv:1106.3383
Source status unknown — claims are unverified
Fabrication of the iron-based superconducting wire using Fe(Se, Te)
similarity 0.91Yoshikazu Mizuguchi et al. · 2009 · arXiv:0906.1636
Source status unknown — claims are unverified
Fabrication and characterization of iron pnictide wires and bulk materials through the powder-in-tube method
similarity 0.88Yanwei Ma et al. · 2009 · arXiv:0906.3114
Source status unknown — claims are unverified
Fabrication of small superconducting coils using (Ba,A)Fe2As2 (A: Na, K) round wires with large critical current densities
similarity 0.88Sunseng Pyon et al. · 2021 · arXiv:2106.10612
Source status unknown — claims are unverified