Effects of carbon concentration and filament number on advanced internal-Mg-infiltration-processed MgB2 Strands
G Z Li, M D Sumption, J B Zwayer, M A Susner, M A Rindfleisch, C J Thong, M J Tomsic, E W Collings
arXiv:1307.1150 · DOI 10.1088/0953-2048/26/9/095007 · 2013-07-03 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
An advanced internal Mg infiltration method (AIMI) in this paper has been shown to be effective in producing superconducting wires containing dense MgB2 layers with high critical current densities. In this study, the in-field critical current densities of a series of AIMI-fabricated MgB2 strands were investigated in terms of C doping levels, heat treatment (HT) time and filament numbers. The highest layer Jc for our monofilamentary AIMI strands is 1.5 x 10^5 A/cm2 at 10 T, 4.2 K, when the C concentration was 3 mol% and the strand was heat-treated at 675 °C for 4 hours. Transport critical currents were also measured at 4.2 K on short samples and one-meter segments of eighteen-filament C-doped AIMI strands. The layer Jcs reached 4.3 x 10^5 A/cm2 at 5 T and 7.1 x 10^4 A/cm2 at 10 T, twice as high as those of the best PIT strands. The analysis of these results indicates that the AIMI strands, possessing both high layer Jcs and engineering Jes after further optimization, have strong potential for commercial applications.
Similar papers
Enhanced higher temperature (20-30 K) transport properties and irreversibility field in nano-Dy2O3 doped advanced internal Mg infiltration processed MgB2 composites
similarity 0.90G. Z. Li et al. · 2014 · arXiv:1409.6185
Source status unknown — claims are unverified
Fabrication of high performance MgB2 wires by an internal Mg diffusion process
similarity 0.89J. M. Hur et al. · 2007 · arXiv:0712.2273
Source status unknown — claims are unverified
Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
similarity 0.88H. L. Suo et al. · 2002 · arXiv:cond-mat/0203114
Source status unknown — claims are unverified
Significantly enhanced critical current densities in MgB2 tapes made by a scaleable, nano-carbon addition route
similarity 0.88Yanwei Ma et al. · 2006 · arXiv:cond-mat/0601223
Source status unknown — claims are unverified
Critical Current Density and n-values of MgB2 Strands over a Wide Range of Temperatures and Fields
similarity 0.88G Z Li et al. · 2011 · arXiv:1108.5775
Source status unknown — claims are unverified
The doping effect of multiwall carbon nanotube on MgB2/Fe superconductor wire
similarity 0.88J. H. Kim et al. · 2006 · arXiv:cond-mat/0603566
Source status unknown — claims are unverified