Reaction method control of impurity scattering in C-doped MgB2, proving the role of defects besides C substitution level

S K Chen, K Y Tan, A S Halim, X Xu, K S B De Silva, W K Yeoh, S X Dou, A Kursumovic, J L MacManus-Driscoll

arXiv:1310.8049 · DOI 10.1088/0953-2048/26/12/125018 · 2013-10-30 · Superconductor Science and Technology

T312 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

In this study, Si and C were incorporated into polycrystalline MgB2 via in situ reaction of Mg and B with either SiC or with separate Si and C (Si+C). The electrical transport and magnetic properties of the two series of samples were compared. The corrected resistivity at 40K, Rho A(40K), is higher for the SiC reacted samples regardless of carbon (C) substitution level, indicating larger intragrain scattering because of the simultaneous reaction between Mg and SiC and carbon substitution during the formation of MgB2. In addition, because of the cleaner reaction route for the SiC reacted samples, the calculated active area that carries current, AF, is twice that of the (Si+C) samples. On the other hand, the upper critical field, Hc2, was similar for both sets of samples despite their different C substitution levels which proves the importance of defect scattering in addition to C substitution level. Hence, the form of the precursor reactants is critical for tuning the form of Hc2(T).