Satoshi Demura, Masashi Tanaka, Aichi Yamashita, Saleem J. Denholme, Hiroyuki Okazaki, Masaya Fujioka, Takahide Yamaguchi, Hiroyuki Takeya, Kazumasa Iida, Bernhard Holzapfel, Hideaki Sakata, Yoshihiko Takano
arXiv:1412.8426 · DOI 10.7566/JPSJ.85.015001 · 2014-12-29
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
FeSe film is successfully fabricated onto Rolling Assisted Biaxially Textured Substrate (RABiTS) tapes by an electrochemical deposition technique. The deposited FeSe films tend to become high crystallinity with a decrease in the applied voltage to -1.0 V, and the compositional ratio of Fe to Se approaches 1:1. The sample deposited at -1.0 V shows a superconducting transition approximately 8.0 K in the magnetic susceptibility.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8 | Pressure not reported | unknown |
Similar papers
Observation of Zero Resistance in As-Electrodeposited FeSe
similarity 0.94Aichi Yamashita et al. · 2017 · arXiv:1711.10273
Source status unknown — claims are unverified
Fe-based superconducting thin films on metallic substrates: growth, characteristics and relevant properties
similarity 0.88Kazumasa Iida et al. · 2018 · arXiv:1812.10264
Source status unknown — claims are unverified
Post-growth Fe deposition on the superconductivity of monolayer FeSe films on SrTiO3−δ
similarity 0.87Xiaotong Jiao et al.
Source status unknown — claims are unverified
Critical Current Density and AC Magnetic Susceptibility of High-quality FeTeSe Superconducting Tapes
similarity 0.86Xin Zhou et al. · 2025 · arXiv:2501.16189
Source status unknown — claims are unverified
Evidence of Inhomogeneous Superconductivity in FeTeSe Thin Film Using Scotch-Tape Method
similarity 0.86H. Okazaki et al. · 2012 · arXiv:1205.2865
Source status unknown — claims are unverified
Iron-chalcogenide FeSeTe coated superconducting tapes for high field applications
similarity 0.86Weidong Si et al. · 2011 · arXiv:1106.2466
Source status unknown — claims are unverified