The calcium doping effects on the structural and electrical properties of NdFeAsO0.8F0.2

F. Shahbaz Tehrani, V. Daadmehr

arXiv:1901.10872 · 2019-01-30 · arXiv: Superconductivity

T1experimental

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We have investigated experimentally how properties of NdFeAsO0.8F0.2 superconductor affected due to the substitution of the calcium by the neodymium. We have synthesized polycrystalline Nd1-xCaxFeAsO0.8F0.2 samples with x=0, 0.01, 0.025, 0.05 and 0.1 through the one step solid state reaction method. The X-ray diffraction patterns, refined using the MAUD software and Rietveld s method, have indicated the formation of tetragonal structure with the space group P4/nmm:2. We studied various structural parameters such as lattice parameters, bond angles, bond length, and etc. Based on the XRD data refinement, we have determined the upper limit of the calcium solubility in Nd-1111 structure and it is restricted to x 0.05. Also, we found that the lattice parameter a was almost constant by increasing the calcium content, while the lattice parameter c and the cell volume decreased. Based on XRD data analysis, we have inference that these are due to the variations in the bond angles of As-Fe-As α and \b{eta} and a decrease in the bond lengths upon increasing x. So, we have expected that the superconducting transition temperature will be sensitive to the calcium doping. Experimentally, the superconducting transition temperature was reduced from 55K (x = 0) to 48K (x = 0.01) and disappeared for other samples. On the other hand, it can be concluded from our study results about of the structural and electrical properties, which the superconducting transition temperature decreased with increasing the distortion of FeAs4-tetrahedrons from regular one. Also, based on Williamson-Hall equation, the microstrain of the samples increased upon increasing x and for Nd0.95Ca0.05FeAsO0.8F0.2 sample was grown approximately three times in comparison to the pure sample. So, it is noticeable that there is a relation between the structural properties and superconductivity in our samples.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
NdFeAsO0.8F0.2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	55	Pressure not reported	unknown
Nd0.99Ca0.01FeAsO0.8F0.2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	48	Pressure not reported	unknown