Boron Content and the Superconducting Critical Temperature of Carbon-Based Materials
Nadina Gheorghiu, Charles R. Ebbing, Timothy J. Haugan
arXiv:2012.06624 · 2020-12-11 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
In this paper, we present results on magnetization properties of boron nitride-carbon (BN-C) and boron carbide-carbon (B4C-C) granular mixtures. The temperature-dependent magnetization for field-cooled during cooling and field-cooled during warming shows a kind of thermal hysteresis that is always seen around a metamagnetic phase transition from an antiferromagnetic martensite to a ferromagnetic austenite phase. The low-temperature magnetization has an upward turn that can be attributed to superparamagnetism, diamagnetic shielding, and trapped flux characteristic to high-temperature superconducting materials. After subtracting the diamagnetic background, the field-dependent magnetization loops M(B) are ferromagnetic-like, more significant for the BN-C than for the B4C-C mixture. In addition, the magnetization loops show the kink feature characteristic to granular superconductivity. The irreversibility temperature for a B4C-C mixture having 37.5 wt% B is Tc = 76 K. Combining our data with previous results on B-doped diamond and Q-carbon, we find that Tc increases linearly with the B concentration.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| B4C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 76 | Pressure not reported | unknown |
Similar papers
Carbon substitution in MgB2 single crystals: Structural and superconducting properties
similarity 0.87S. M. Kazakov et al.
Source status unknown — claims are unverified
Heavy boron doping in superconducting carbon materials
similarity 0.87Yuki Sakai et al.
Source status unknown — claims are unverified
Carbon substitution in MgB2 single crystals: structural and superconducting properties
similarity 0.87S. M. Kazakov et al. · 2004 · arXiv:cond-mat/0405060
Source status unknown — claims are unverified
Systematic Effects of Carbon Doping on the Superconducting Properties of Mg(B1−xCx)2
similarity 0.86R. H. T. Wilke et al.
Source status unknown — claims are unverified
Simulating the effect of boron doping in superconducting carbon
similarity 0.86Yuki Sakai et al. · 2017 · arXiv:1709.07125
Source status unknown — claims are unverified
Two types of magnetism in the magnetic superconductor TmNi2B2C related to the degree of carbon-site occupancy
similarity 0.85A. M. Mulders et al.
Source status unknown — claims are unverified