Flux-Pinning Behaviors and Mechanism According to Dopant Level in (Fe, Ti) Paticle-Doped MgB$_2$ Superconductor
H. B. Lee, G. C. Kim, Young Jin Shon, Dongjin Kim, Y. C. Kim
arXiv:2012.11146 · 2020-12-21
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We have studied flux-pinning effects of MgB$_2$ superconductor by doping (Fe, Ti) particles of which radius is 163 nm on average. 5 wt.\% (Fe, Ti) doped MgB$_2$ among the specimens showed the best field dependence of magnetization and 25 wt.\% one did the worst at 5 K . The difference of field dependence of magnetization of the two increased as temperature increased. Here we show experimental results of (Fe, Ti) particle-doped MgB$_2$ according to dopant level and the causes of the behaviors. Flux-pinning effect of volume defects-doped superconductor was modeled in ideal state. During the study, we had to divide M-H curve of volume defect-dominating superconductor as three discreet regions for analyzing flux pinning effects, which are diamagnetic increase region, $Δ$H=$Δ$B region, and diamagnetic decrease region. As a result, flux-pinning effects of volume defects decreased as dopant level increased over the optimal dopant level, which was caused by decrease of flux-pinning limit of a volume defect. And similar behaviors are obtained as dopant level decreased below the optimal dopant level, which was caused by the decreased number of volume defects. Comparing the theory with experimental results, deviations increased as dopant level increased over the optimal dopant level, whereas the two was well matched on less dopant level than the optimal dopant level. The behavior is considered to be caused by segregation of volume defects. On the other hand, the property of over-doped specimens dramatically decrease as temperature increases, which is caused by double decreases of flux-pinning limit of a volume defect and segregation effect.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Increases of a Diamagnetic Property by Flux-Pinning in Volume Defect-Dominating Superconductors
similarity 0.91H. B. Lee et al. · 2019 · arXiv:1904.06434
Source status unknown — claims are unverified
Upper Critical Field Based on the Width of H = B region in a Superconductor
similarity 0.91H. B. Lee et al. · 2019 · arXiv:1905.08559
Source status unknown — claims are unverified
Water-Quenched Effects of 5 wt.% (Fe, Ti) particle-doped MgB Superconductor and Low Limit of Pinning Effect
similarity 0.90H. B. Lee et al. · 2019 · arXiv:1906.05943
Source status unknown — claims are unverified
Delta H = Delta B region in volume defect-dominating superconductor
similarity 0.90H. B. Lee et al. · 2018 · arXiv:1805.04683
Source status unknown — claims are unverified
Quantum Bit Behavior of Pinned Fluxes on Volume Defects in a Superconductor
similarity 0.90H. B. Lee et al. · 2022 · arXiv:2201.06016
Source status unknown — claims are unverified
Superconductivity, critical current density, and flux pinning in MgB_{2-x}(SiC)_{x/2} superconductor after SiC nanoparticle doping
similarity 0.89S. X. Dou et al. · 2002 · arXiv:cond-mat/0207093
Source status unknown — claims are unverified