Superconductivity in In-doped AgPbBiTe3 compounds synthesized by high-pressure synthesis

Sawahara, Takahiro; Arima, Hiroto; Katase, Takayoshi; Yamashita, Aichi; Higashinaka, Ryuji; Mizuguchi, Yoshikazu

doi:10.1016/j.physc.2023.1354308

← Back to search

Superconductivity in In-doped AgPbBiTe3 compounds synthesized by high-pressure synthesis

Sawahara, Takahiro, Arima, Hiroto, Katase, Takayoshi, Yamashita, Aichi, Higashinaka, Ryuji, Mizuguchi, Yoshikazu

arXiv:2306.08338 · DOI 10.1016/j.physc.2023.1354308 · 2023-08-09

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

NaCl-type metal tellurides (MTe) have been widely studied due to unique physical properties. We investigated the In-doping effects on structural and physical properties of Na-Cl type (AgPbBi)(1-x)/3InxTe and the superconducting properties of the In-doped samples. Polycrystalline samples with x = 0-0.5 were synthesized by utilizing high-pressure synthesis. For x = 0.2-0.5, superconductivity was observed in magnetization measurements, where the highest transition temperature (Tc) was 2.8 K for x = 0.4. We measured specific heat for x = 0.4 and confirmed the bulk nature of the superconductivity. The evolution of the Seebeck coefficient and lattice constant by In doping suggests that In valence state is In+3, and the In doping generates electron carriers in the (AgPbBi)(1-x)/3InxTe system.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
(AgPbBi)0.2In0.4Te Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.8	Pressure not reported	unknown
(AgPbBi)0.2In0.4Te Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.8	Pressure not reported	unknown