Optimization of Synthesis Parameters and Superconducting Properties of GdFeAsO1-xFx
Azam, Mohammad, Manasa, Manasa, Zajarniuk, Tatiana, Stelmakh, Svitlana, Cetner, Tomasz, Morawski, Andrzej, Wiśniewski, Andrzej, Singh, Shiv J.
arXiv:2311.13312 · DOI 10.1109/TASC.2023.3341858 · 2023-12-21
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
REFeAsO (RE1111; RE: rare earth) belongs to the 1111 family of iron-based superconductors (FBS), which illustrates the enhancement of the superconducting transition (Tc) with smaller radii of RE. However, the synthesis of the 1111 phase with a heavy rare-earth is always challenging. In this paper, we report the optimization of the growth and superconducting properties of F-doped GdFeAsO1-xFx bulks by preparing the samples in a wide temperature range (700-1100°C) at ambient pressure. The optimized synthesis parameters are concluded based on structural, microstructural, transport, and magnetic measurements. These findings suggest that the optimal conditions for preparing F-doped Gd1111 bulks involve a two-step process at 900°C for 61 hours at ambient pressure, which is lower than previously reported. The optimized samples have revealed the superconducting transition temperature (Tconset) of 43 K for GdFeAsO0.83F0.17. The first-time reported critical current Jc value for this Gd1111 is observed of the order of 10^3 (A/cm^2) at 0 T and 5 K. Our investigation also concluded that highly pure precursors, particularly gadolinium metal, are required to achieve the superconducting properties of F-doped Gd1111. A high growth pressure of 1 GPa reduces the superconducting properties of F-doped Gd1111.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| GdFeAsO0.83F0.17 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 43 | Pressure unresolved | onset |
Similar papers
Magnetic and Superconducting Properties of FeAs-based High-Tc Superconductors with Gd
similarity 0.89E. P. Khlybov et al. · 2009 · arXiv:0909.1937
Source status unknown — claims are unverified
Complete electronic phase diagram and enhanced superconductivity in fluorine-doped PrFeAsO1-xFx
similarity 0.88Priya Singh et al. · 2026 · arXiv:2602.07481
Source status unknown — claims are unverified
Superconductivity and Magnetism in REFeAsO1-xFx (RE=Rare Earth Elements)
similarity 0.88K Kadowaki et al. · 2008 · arXiv:0808.0289
Source status unknown — claims are unverified
Transition Temperature and Upper Critical Field in SmFeAsO1-xFx Synthesized at Low Heating Temperatures
similarity 0.87S. J. Singh et al. · 2013 · arXiv:1303.4163
Source status unknown — claims are unverified
Superconductivity at 36 K in Gadolinium-arsenide Oxides GdOFFeAs
similarity 0.87Peng Cheng et al. · 2008 · arXiv:0804.0835
Source status unknown — claims are unverified
Thorium-doping induced superconductivity up to 56 K in Gd1-xThxFeAsO
similarity 0.87Cao Wang et al. · 2008 · arXiv:0804.4290
Source status unknown — claims are unverified