Structural and resistivity properties of Fe$_{1-x}$Co${_x}$Se single crystals grown by the molten salt method

Qiaoyu Wang; Mingwei Ma; Binbin Ruan; Menghu Zhou; Yadong Gu; Qingsong Yang; Lewei Chen; Yunqing Shi; Junkun Yi; Genfu Chen; Zhian Ren

doi:10.1016/j.jcrysgro.2024.127633

Structural and resistivity properties of Fe$_{1-x}$Co${_x}$Se single crystals grown by the molten salt method

Qiaoyu Wang, Mingwei Ma, Binbin Ruan, Menghu Zhou, Yadong Gu, Qingsong Yang, Lewei Chen, Yunqing Shi, Junkun Yi, Genfu Chen, Zhian Ren

arXiv:2402.14436 · DOI 10.1016/j.jcrysgro.2024.127633 · 2024-02-22 · Journal of Crystal Growth

T3experimental3 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

A series of tetragonal Fe$_{1-x}$Co${_x}$Se single crystals with a complete Co doping range (0$\leq$x$\leq$0.52) up to its solid solubility limit in FeSe have been grown by an eutectic AlCl${_3}$/KCl molten salt method. The typical lateral size of as-grown Fe$_{1-x}$Co${_x}$Se single crystals is 1$-$5 mm. The chemical composition and homogeneity of the crystals was examined by both inductively coupled plasma atomic emission spectroscopy and energy dispersive spectrometer. X-ray diffraction analysis demonstrates that the crystal lattice parameters $a$ and $c$ are both linearly decreased with increasing Co doping level x. In the whole doping range, all the samples show metallic behaviour in contrast to a metal insulator transition of Cu-doped FeSe according to the resistivity measurements