Electrical transport properties of bulk MgB2 materials synthesized by the electrolysis on fused mixtures of MgCl2, NaCl, KCl and MgB2O4
Kenji Yoshii, Hideki Abe
arXiv:cond-mat/0204208 · DOI 10.1088/0953-2048/15/10/101 · 2002-04-09 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Electrolysis was carried out on fused mixtures of MgCl2, NaCl, KCl and MgB2O4 under an Ar flow at 600C. Electrical resistivity measurements for the grown deposits show an onset of superconducting transition at 37 K in the absence of applied magnetic field. The resistivity decreases down to zero below 32 K. From an applied-field dependence of resistivity, an upper critical field and a coherence length were calculated to be 9.7 T and 5.9 nm at 0 K, respectively.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 37 | Pressure unresolved | onset |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 32 | Pressure unresolved | zero_resistance |
Similar papers
Electrochemical Synthesis of Superconductive Boride MgB2 from Molten Salts
similarity 0.89Hideki Abe & Kenji Yoshii · 2002 · arXiv:cond-mat/0204169
Source status unknown — claims are unverified
Superconducting Properties of MgB2 Bulk Materials Prepared by High Pressure Sintering
similarity 0.89Y. Takano et al. · 2001 · arXiv:cond-mat/0102167
Source status unknown — claims are unverified
The upper critical field in superconducting MgB_2
similarity 0.88K. -H. Müller et al. · 2001 · arXiv:cond-mat/0102517
Source status unknown — claims are unverified
Temperature- and magnetic-field-dependent resistivity of MgB2 sintered at high temperature and high pressure condition
similarity 0.88C. U. Jung et al. · 2001 · arXiv:cond-mat/0102215
Source status unknown — claims are unverified
Electrical and structural properties of MgB2 films prepared by sequential deposition of B and Mg on the NbN buffered Si(100) substrate
similarity 0.87S. Chromik et al. · 2004 · arXiv:cond-mat/0401569
Source status unknown — claims are unverified
High critical current densities in superconducting MgB2 thin films
similarity 0.87S. H. Moon et al. · 2001 · arXiv:cond-mat/0104230
Source status unknown — claims are unverified