Structure and Superconductivity in Zr-Stabilized, Nonstoichiometric Molybdenum Diboride
L. E. Muzzy, M. Avdeev, G. Lawes, M. K. Haas, H. W. Zandbergen, A. P. Ramirez, J. D. Jorgensen, R. J. Cava
arXiv:cond-mat/0206006 · DOI 10.1016/S0921-4534(02)01861-0 · 2002-05-31 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The structure and physical properties of the Zr-stabilized, nonstoichiometric molybdenum diboride superconductor are reported. Good quality material of the diboride structure type can only be obtained by partial substitution of Zr for Mo, and the quenching of melts. The phase is best made with boron in excess of the ideal 2:1 boron to metal ratio. Powder neutron diffraction measurements show that the non-stoichiometry is accommodated by atom deficiency in the metal layers. The diboride structure type exists for (Mo.96Zr.04)xB2 for x between 0.85 and 1.0. Electron diffraction shows that the stoichiometric material, x=1, has a significant number of stacking faults. Tc increases from 5.9 to 8.2K with the introduction of metal vacancies. Resistivity measurements indicate that (Mo.96Zr.04).88B2 is a bad metal, and specific heat measurements show that gamma= 4.4 mJ/mol K2, and that deltaC/gammaTc = 1.19. Preliminary boron isotope effect measurements indicate an exponent 0.11(5). Analysis of the data in terms of the electronic structure is reported, allowing an estimate of the electron-phonon coupling constant, lamda = 0.1-0.3, making these weak-coupling superconductors. Preliminary characterizations of the superconductivity in the related phases NbxB2 and (Mo.96X.04).85B2 for X=Ti, and Hf are reported.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| (Mo0.96Zr0.04)0.88B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.2 | Pressure not reported | unknown |
| (Mo0.96Zr0.04)0.88B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 8.2 | Pressure not reported | unknown |
Similar papers
Diboride compounds doped with transition metalsa route to superconductivity through structure stabilization as well as defects
similarity 0.88P. M. Dee et al. · 2023 · arXiv:2310.03818
Source status unknown — claims are unverified
Doping-induced superconductivity of ZrB2 and HfB2
similarity 0.88N. Barbero et al.
Source status unknown — claims are unverified
Effect of metal vacancies on the electronic band structure of hexagonal Nb, Zr and Y diborides
similarity 0.88I. R. Shein et al. · 2002 · arXiv:cond-mat/0211247
Source status unknown — claims are unverified
Pair weakening in mixed rare-earth nickel borocarbides (R,R')Ni2B2C
similarity 0.86J. Freudenberger et al. · 2008 · arXiv:0811.1694
Source status unknown — claims are unverified
Discovery of superconductivity in technetium-borides at moderate pressures
similarity 0.86Xiangru Tao et al. · 2024 · arXiv:2403.15283
Source status unknown — claims are unverified
Magnetism and superconductivity in 3d-metal-substituted Bi-based cuprates having the 2:2:0:1 structure
similarity 0.86K. Remschnig et al.
Source status unknown — claims are unverified