Microwave performance of high-density bulk MgB2
A. T. Findikoglu, A. Serquis, L. Civale, X. Z. Liao, Y. T. Zhu, M. E. Hawley, F. M. Mueller, V. F. Nesterenko, Y. Gu
arXiv:cond-mat/0303283 · DOI 10.1063/1.1590739 · 2003-03-14 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We have performed microwave measurements on superconducting hot-isostatically- pressed (HIPed) bulk MgB2 using a parallel-plate resonator technique. The high density and strength of the HIPed material allowed preparation of samples with mirror-like surfaces for microwave measurements. The microwave surface resistance decreased by about 40% at 20 K when the root-mean-square surface roughness was reduced from 220 nm to 110 nm through surface-polishing and ion-milling. The surface resistance was independent of surface microwave magnetic field at least up to 4 Oe and below 30 K. We attribute this behavior, and the overall low surface resistance (~0.8 mOhms at 10 GHz and 20 K), to the high density of our samples and the absence of weak links between grains.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Study of the microwave electrodynamic response of MgB2 thin films
similarity 0.90A. Andreone et al. · 2001 · arXiv:cond-mat/0109465
Source status unknown — claims are unverified
Significant Reduction of the Microwave Surface Resistance of MgB2 Films by Surface Ion Milling
similarity 0.89Sang Young Lee et al. · 2001 · arXiv:cond-mat/0105327
Source status unknown — claims are unverified
Microwave surface resistance of pristine and neutron-irradiated MgB2 samples in magnetic field
similarity 0.88M. Bonura et al. · 2007 · arXiv:0709.0618
Source status unknown — claims are unverified
Superconducting properties of well-shaped MgB2 single crystals
similarity 0.87Kijoon H. P. Kim et al.
Source status unknown — claims are unverified
Electrodynamic response of MgB2 sintered pellets and thin films
similarity 0.87A. Andreone et al. · 2001 · arXiv:cond-mat/0110640
Source status unknown — claims are unverified
Thick MgB2 film with (101) oriented micro-crystals
similarity 0.86Chinping Chen et al. · 2004 · arXiv:cond-mat/0406325
Source status unknown — claims are unverified