The contribution of 211 particles to the mechanical reinforcement mechanism of 123 superconducting single domains

J. -P. Mathieu; I. G. Cano; T. Koutzarova; A. Rulmont; Ph. Vanderbemden; D. Dew-Hughes; M. Ausloos; R. Cloots

doi:10.1088/0953-2048/17/1/030

← Back to search

The contribution of 211 particles to the mechanical reinforcement mechanism of 123 superconducting single domains

J. -P. Mathieu, I. G. Cano, T. Koutzarova, A. Rulmont, Ph. Vanderbemden, D. Dew-Hughes, M. Ausloos, R. Cloots

arXiv:cond-mat/0310071 · DOI 10.1088/0953-2048/17/1/030 · 2003-10-03 · Superconductor Science and Technology

T321 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Hardness and fracture toughness of Dy-123 single-domains were studied by Vickers micro-indentation. A significant anisotropy of the mechanical properties was observed. Hardness tests give higher values when performed in (001) planes rather than in planes parallel to the c-axis. Moreover cracks pattern around the indentation follows preferential orientation in planes parallel to the c-axis whereas a classical ''four-cracks'' pattern is observed in the (001) planes. It has been possible to show the crucial role played by the 211-particles in the deviating mechanism of cracks and the relevance of the 211-particle distribution high homogeneity in the material.