RF Surface Resistance of a HIPped MgB2 Sample at 21 GHz
T. Tajima, F. L. Krawczyk, J. Liu, D. C. Nguyen, D. L. Schrage, A. Serquis, A. H. Shapiro, V. F. Nesterenko, Y. Gu
arXiv:cond-mat/0310213 · 2003-10-09 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Magnesium diboride (MgB2) is attractive for RF cavity application for particle accelerators because it might not show an increase of RF surface losses at high magnetic surface fields, a phenomenon that has prevented high-Tc superconducting materials such as YBCO from being used for this application. We have measured the RF surface resistance (Rs) at 21 GHz of a MgB2 sample fabricated using Hot Isostatic Press (HIP) at 200 MPa and 1000 C. The results show that polishing with 0.1-micron diamond lapping film followed by a 1500-psi DI water rinse in a clean room reduced the Rs by a factor of 6.2 at 15 K and it is the lowest compared to other published data. The Rs data near the lowest temperature (~13 K) scatter between 0.6 and 1.3 mOhm. The penetration depth and energy gap were estimated to be 263 nm and 1.9-2.7, respectively, for the polished surface.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | 0.2 GPa | unknown |
Similar papers
Superconducting magnesium diboride coatings for radio frequency cavities fabricated by hybrid physical-chemical vapor deposition
similarity 0.89M. A. Wolak et al.
Source status unknown — claims are unverified
Effects of Ion Milling on the Microwave Properties of MgB2 Films
similarity 0.88Sang Young Lee et al. · 2002 · arXiv:cond-mat/0208304
Source status unknown — claims are unverified
Significant Reduction of the Microwave Surface Resistance of MgB2 Films by Surface Ion Milling
similarity 0.88Sang Young Lee et al. · 2001 · arXiv:cond-mat/0105327
Source status unknown — claims are unverified
MgB2 nonlinear properties investigated under localized high rf magnetic field excitation-report 2
similarity 0.87Tamin Tai et al. · 2013 · arXiv:1309.1706
Source status unknown — claims are unverified
Study of the microwave electrodynamic response of MgB2 thin films
similarity 0.87A. Andreone et al. · 2001 · arXiv:cond-mat/0109465
Source status unknown — claims are unverified
Microwave surface resistance of pristine and neutron-irradiated MgB2 samples in magnetic field
similarity 0.86M. Bonura et al. · 2007 · arXiv:0709.0618
Source status unknown — claims are unverified