Stoichiometry control of magnetron sputtered Bi$_2$Sr$_2$Ca$_{1-x}$Y$_x$Cu$_2$O$_y$ (0$\le$x$\le$0.5) thin film, composition spread libraries: Substrate bias and gas density factors
R. J. Sanderson, K. C. Hewitt
arXiv:cond-mat/0504442 · DOI 10.1016/j.physc.2005.06.002 · 2005-04-18 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A magnetron sputtering method for the production of thin-film libraries with a spatially varying composition, x, in Bi2Sr2Ca1-xYxCu2Oy (0<=x<=0.5) has been developed. Two targets with a composition of Bi2Sr2YCu2O_{8.5 + δ} and Bi_2Sr_2CaCu_2O_{8 + δ} are co-sputtered with appropriate masks. The target masks produce a linear variation in opposite, but co-linear radial direction, and the rotation speed of the substrate table is sufficient to intimately mix the atoms. EDS/WDS composition studies of the films show a depletion of Sr and Bi that is due to oxygen anion resputtering. The depletion is most pronounced at the centre of the film (i.e. on-axis with the target) and falls off symmetrically to either side of the 75 mm substrate. At either edge of the film the stoichiometry matches the desired ratios. Using a 12 mTorr process gas of argon and oxygen in a 2:1 ratio, the strontium depletion is corrected. The bismuth depletion is eliminated by employing a rotating carbon brush apparatus which supplies a -20 V DC bias to the sample substrate. The negative substrate bias has been used successfully with an increased chamber pressure to eliminate the resputtering effect across the film. The result is a thin film composition spread library with the desired stoichiometry.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Bi2Sr2CaCu2O8+δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 67 | Pressure not reported | onset |
Similar papers
Magnetron Sputter deposition of a 48-member cuprate superconductor library: Bi2Sr2YxCa1-xCu2Oy (0.5 <= x <= 1) linearly varying in steps of 0.01
similarity 0.86R. J. Sanderson & K. C. Hewitt · 2007 · arXiv:cond-mat/0702035
Source status unknown — claims are unverified
Doping dependence of the critical current in Bi2Sr2CaCu2Oy
similarity 0.85Muntaser Naamneh et al. · 2014 · arXiv:1411.6393
Source status unknown — claims are unverified
Deviations from plastic barriers in BiSrCaCuO thin films
similarity 0.85Y. Z. Zhang et al. · 2004 · arXiv:cond-mat/0408555
Source status unknown — claims are unverified
Transmission Electron Study of Heteroepitaxial Growth in the BiSrCaCuO System
similarity 0.85A. Chaiken et al. · 1996 · arXiv:cond-mat/9601090
Source status unknown — claims are unverified
Interplay of doping and structural modulation in superconducting Bi2Sr2−xLaxCuO6+δ thin films
similarity 0.84Z. Z. Li et al.
Source status unknown — claims are unverified
Effect of chemical inhomogeneity in the bismuth-based copper oxide superconductors
similarity 0.84H. Eisaki et al. · 2003 · arXiv:cond-mat/0312570
Source status unknown — claims are unverified