Strong influence of boron precursor powder on the critical current density of MgB2
S. K. Chen, K. A. Yates, M. G. Blamire, J. L. MacManus-Driscoll
arXiv:cond-mat/0507652 · DOI 10.1088/0953-2048/18/11/011 · 2005-07-27 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The influence of the nature of the boron precursor on the superconducting properties of polycrystalline MgB2 was studied. Critical current densities for the MgB2 made from high purity amorphous boron are at least a factor of three higher than typical values measured for standard MgB2 samples made from amorphous precursors. Two possible mechanisms are proposed to account for this difference. Samples made from crystalline boron powders have around an order of magnitude lower Jc compared to those made from amorphous precursors. X-ray, Tc and resistivity studies indicate that this is as a result of reduced current cross section due to the formation of Mg-B-O phases. The samples made from amorphous B contain far fewer Mg-B-O phases than crystalline B despite the fact that the amorphous B contains more B2O3. The different reactivity rates of the precursor powders accounts for this anomaly.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Strong influence of precursor powder on the critical current density of Fe-sheathed MgB2 tapes
similarity 0.93Dongliang Wang et al. · 2007 · arXiv:0710.1407
Source status unknown — claims are unverified
Effects of Boron Purity, Mg Stoichiometry and Carbon Substitution on Properties of Polycrystalline MgB
similarity 0.88R. A. Ribeiro et al. · 2002 · arXiv:cond-mat/0212385
Source status unknown — claims are unverified
A novel process to produce amorphous nano-sized B useful for MgB2 phase synthesis
similarity 0.87Maurizio Vignolo et al. · 2014 · arXiv:1405.4112
Source status unknown — claims are unverified
Influence of the carbon substitution on the critical current density and AC losses in MgB2 single crystals
similarity 0.87M. Ciszek et al. · 2011 · arXiv:1101.2596
Source status unknown — claims are unverified
Resistivity and Magneto-Optical Evidence for Variable and Incomplete Connectivity in Dense, High Critical Current Density C-alloyed Magnesium Diboride
similarity 0.87Senkowicz, B. J. et al. · 2006 · arXiv:cond-mat/0603800
Source status unknown — claims are unverified
Higher borides and oxygen-enriched Mg-B-O inclusions as possible pinning centers in nanostructural magnesium diboride and the influence of additives on their formation
similarity 0.87Tatiana Prikhna et al. · 2010 · arXiv:1001.1904
Source status unknown — claims are unverified