Compressibility and thermal expansion of YBa2Cu3Ox

K. Grube, H. Leibrock, W. H. Fietz, S. I. Schlachter, A. I. Rykov, S. Tajima, P. Schweiss, B. Obst, H. Wuehl

arXiv:cond-mat/9912359 · DOI 10.1023/A:1022567327685 · 1999-12-20 · Journal of Low Temperature Physics

T35 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The linear compressibilities and the thermal expansion of an untwinned, nearly optimal doped YBa2Cu3O6.94 single crystal were measured along the three crystallographic axes with a high-resolution dilatometer mounted in a high-pressure cell. The measurements were performed in a temperature range from 50 K to 320 K under hydrostatic gas pressure of maximal 0.65 GPa. At a temperature of 300 K the measured bulk modulus is reduced and shows a very strong enhancement under increasing pressure due to pressure-induced oxygen ordering. This ordering process can also be related to a glass transition seen in the thermal expansion above 225 K. At lower temperatures, when oxygen ordering is frozen, the bulk modulus is increased and shows a significantly reduced enhancement under pressure. This pressure dependence, however, is still anomalous high, probably caused by bonds of extremely different compressibilities within the unit cell. The widely spread literature data of the bulk modulus can be explained by this high pressure dependence.