Carbon Doping of MgB2 by Toluene and Malic-Acid-in-Toluene
S. D. Bohnenstiehl, M. A. Susner, Y. Yang, E. W. Collings, M. D. Sumption, M. A. Rindfleisch, R. Boone
arXiv:1010.0925 · 2010-10-05
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The decomposition of malic acid in the presence of Mg and B was studied using Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TGA) which revealed that malic acid reacted with Mg but not B. Also, the addition of toluene to dissolve malic acid followed by subsequent drying resulted in no reaction with Mg, indicating that the malic acid had decomposed during the dissolution/drying stage. The total carbon contributed by toluene versus a toluene/5 wt% malic acid mixture was measured using a LECO CS600 carbon analyzer. The toluene sample contained ~0.4 wt% C while the toluene/malic acid mixture had ~1.5 wt% C, demonstrating that the toluene contributed a significant amount of carbon to the final product. Resistivity measurements on powder-in-tube MgB2 monofilamentary wires established that the toluene/malic acid doped sample had the highest Bc2. However, the toluene-only sample had the highest transport Jc over most of the magnetic field range (0-9 T), equaled only by that of toluene/malic acid sample in fields above 9 T.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Improvement of Critical Current Density and Upper Critical Field in MgB2 using Carbohydrate
similarity 0.86J. H. Kim et al. · 2006 · arXiv:cond-mat/0612472
Source status unknown — claims are unverified
Influence of Strand Design, Boron Type, and Carbon Doping Method on the Transport Properties of Powder-in-Tube MgB2-XCX Strands
similarity 0.86Y. Yang et al. · 2011 · arXiv:1109.4333
Source status unknown — claims are unverified
Effects of Boron Purity, Mg Stoichiometry and Carbon Substitution on Properties of Polycrystalline MgB
similarity 0.84R. A. Ribeiro et al. · 2002 · arXiv:cond-mat/0212385
Source status unknown — claims are unverified
Superconducting Properties of adipic acid doped Bulk MgB2 Superconductor
similarity 0.84Arpita Vajpayee et al. · 2008 · arXiv:0811.2646
Source status unknown — claims are unverified
Carbon doping of superconducting magnesium diboride
similarity 0.84R. A. Ribeiro et al. · 2002 · arXiv:cond-mat/0210530
Source status unknown — claims are unverified
Properties of MgB2 thin films with carbon doping
similarity 0.84A. V. Pogrebnyakov et al. · 2004 · arXiv:cond-mat/0407146
Source status unknown — claims are unverified