Influence of Strand Design, Boron Type, and Carbon Doping Method on the Transport Properties of Powder-in-Tube MgB2-XCX Strands
Y. Yang, M. Susner, M. D. Sumption, M. Rindfleisch, M. Tomsic, E. W. Collings
arXiv:1109.4333 · DOI 10.1109/TASC.2012.2184539 · 2011-09-20 · IEEE Transactions on Applied Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The transport properties of a number of MgB2 strands have been investigated in terms of their response to strand design, starting B powder choice, and the approach to C doping used. The strands had various designs, specifically; (i) several chemical barriers were introduced, viz: Fe and Nb, (ii) the strands were encased in various outer-sheath materials, viz.: monel, Cu+monel, monel+glidcop, Nb+monel, (iii) the filament counts were varied (1, 18, and 36), and (iv) the final strand diameter was varied. In addition, for a subset of the strand designs several B powder and C-dopant types were investigated. Specifically, two types of amorphous B powder were used: (i) Moissan based "Tangshan boron" (ii) "SMI-boron" which is produced in a plasma torch by the reduction-by-hydrogen of BCl3. Two approaches to C doping were taken: (i) "malic-acid treatment" in which C is introduced into the B powder precursor by the moderate temperature drying out a slurry of B mixed in with a malic-acid-toluene solution (during which the malic acid decomposes leaving C as the only solid residue) before the Mg powder is mixed in; (ii) direct C doping of the SMI-produced B by introducing a known percentage of CH4 into the plasma flame. Critical current densities, Jc, were measured on 1.5 m long samples at 4.2 K in fields of up to 14 T; of all the strands measured, that doped with SMI-C at a nominal 4 mol% C (in relation B) yielded the highest Jc values e.g 1.1x105 A/cm2 at 7 T, 4.5x104 at 10 T, and 2.2x104 A/cm2 at 12 T. The n-values are given for all strands at 5 and 10 T, and for a certain set of strands the magnetic field dependencies of the n-values and the influence of C-doping is presented. Finally we demonstrate that, over a wide range of B, log(Jc) decreases linearly with B with a slope -α such that the Jc(B) of any strand can be parameterized in terms of α and its zero-field intercept Jc(B=0).
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Critical Current Density and n-values of MgB2 Strands over a Wide Range of Temperatures and Fields
similarity 0.90G Z Li et al. · 2011 · arXiv:1108.5775
Source status unknown — claims are unverified
CVD routes to MgB2 conductors
similarity 0.89D. K. Finnemore et al. · 2003 · arXiv:cond-mat/0302242
Source status unknown — claims are unverified
Transport and magnetic Jc of MgB2 strands and small helical coils
similarity 0.88M. D. Sumption et al. · 2004 · arXiv:cond-mat/0409651
Source status unknown — claims are unverified
Development of Doped MgB2 Wires and Tapes for Practical Applications
similarity 0.88Zhaoshun Gao et al. · 2010 · arXiv:1001.1219
Source status unknown — claims are unverified
Systematic effects of carbon doping on the superconducting properties of Mg(BC)
similarity 0.88R. H. T. Wilke et al. · 2003 · arXiv:cond-mat/0312235
Source status unknown — claims are unverified
Improved critical current densities in B4C doped MgB2 based wires
similarity 0.87P. Lezza et al. · 2006 · arXiv:cond-mat/0607073
Source status unknown — claims are unverified