Effects of the sintering atmosphere on the superconductivity of SmFeAsO1-xFx compounds
Y. Ding, Y. Sun, X. D. Wang, J. C. Zhuang, L. J. Chui, Z. X. Shi
arXiv:1102.5571 · DOI 10.1088/0953-2048/24/9/095014 · 2011-02-28 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A series of SmFeAsO1-xFx samples were sintered in quartz tubes filled with air of different pressures. The effects of the sintering atmosphere on the superconductivity were systematically investigated. The SmFeAsO1-xFx system maintains a transition temperature (Tc) near 50 K until the concentration of oxygen in quartz tubes increases to a certain threshold, after which Tc decreases dramatically. Fluorine losses, whether due to vaporization, reactions with starting materials, and reactions with oxygen, proved to be detrimental to the superconductivity of this material. The deleterious effects of the oxygen in the sintering atmosphere were also discussed in detail.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| SmFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 50 | Pressure not reported | unknown |
Similar papers
Transition Temperature and Upper Critical Field in SmFeAsO1-xFx Synthesized at Low Heating Temperatures
similarity 0.89S. J. Singh et al. · 2013 · arXiv:1303.4163
Source status unknown — claims are unverified
One step synthesis of SmO1-xFxFeAs bulks with Tc = 54.6 K: High upper critical field and critical current density
similarity 0.87Yanwei Ma et al. · 2008 · arXiv:0806.2839
Source status unknown — claims are unverified
Oxygen-annealing effects on superconductivity in polycrystalline Fe1-xTe1-ySey
similarity 0.86Gina M. Friederichs et al. · 2015 · arXiv:1505.06066
Source status unknown — claims are unverified
Superconductivity above 30 K due to the introduction of oxygen in CaFeAsF
similarity 0.86Yixin Liu et al. · 2023 · arXiv:2311.07943
Source status unknown — claims are unverified
Copper doping effects on the superconducting properties of Sm-based oxypnictides
similarity 0.86Mohammad Azam et al. · 2024 · arXiv:2404.06146
Source status unknown — claims are unverified
Superconductivity induced by U doping in the SmFeAsO system
similarity 0.86Bo Huang et al.
Source status unknown — claims are unverified