Thin film growth by pulsed laser deposition and properties of 122-type iron-based superconductor AE(Fe1--xCox)2As2 (AE = alkaline earth)
Katase, Takayoshi, Hiramatsu, Hidenori, Kamiya, Toshio, Hosono, Hideo
arXiv:1205.4103 · DOI 10.1088/0953-2048/25/8/084015 · 2012-08-23
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
This paper reports comprehensive results on thin-film growth of 122-type iron-pnictide superconductors, AE(Fe1-xCox)2As2 (AE = Ca, Sr, and Ba, AEFe2As2:Co) by a pulsed laser deposition method using a neodymium-doped yttrium aluminum garnet laser as an excitation source. The most critical parameter to produce the SrFe2As2:Co and BaFe2As2:Co phases is the substrate temperature (Ts). It is difficult to produce highly-pure CaFe2As2:Co phase thin film at any Ts. For BaFe2As2:Co epitaxial films, controlling Ts at 800-850 °C and growth rate to 2.8-3.3 Å/s produced high-quality films with good crystallinity, flat surfaces, and high critical current densities > 1 MA/cm2, which were obtained for film thicknesses from 100 to 500 nm. The doping concentration x was optimized for Ba(Fe1-xCox)2As2 epitaxial films, leading to the highest critical temperature of 25.5 K in the epitaxial films with the nominal x = 0.075.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Ba(Fe1-xCox)2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 25.5 | Pressure not reported | unknown |
Similar papers
Advanced surface characterization of Ba(FeCo)As epitaxial thin films
similarity 0.89D. Daghero et al. · 2016 · arXiv:1609.00304
Source status unknown — claims are unverified
Localized High Frequency Electrodynamic Behavior of Optimally-doped Ba(FeCo)As Single Crystal films
similarity 0.88Tamin Tai et al. · 2015 · arXiv:1507.03318
Source status unknown — claims are unverified
Epitaxial Growth of NdFeAsO Thin Films by Molecular Beam Epitaxy
similarity 0.88T. Kawaguchi et al. · 2009 · arXiv:0907.3108
Source status unknown — claims are unverified
Scaling behaviour of the critical current in clean epitaxial Ba(Fe1-xCox)2As2 thin films
similarity 0.88Iida, K. et al. · 2010 · arXiv:1001.2505
Source status unknown — claims are unverified
Discovery of a novel 112-type iron-pnictide and La-doping induced superconductivity in Eu1-xLaxFeAs2 (x = 0 ~ 0.15)
similarity 0.88Yu, Jia et al. · 2017 · arXiv:1611.06821
Source status unknown — claims are unverified
Upper critical field of the 122-type iron pnictide superconductors
similarity 0.88L. Jiao et al. · 2011 · arXiv:1101.3150
Source status unknown — claims are unverified