Phase diagram and superconductivity at 58.1 K in α-FeAs free SmFeAsO1-xFx
Masaya Fujioka, Saleem James Denholme, Toshinori Ozaki, Hiroyuki Okazaki, Keita Deguchi, Satoshi Demura, Hiroshi Hara, Tohru Watanabe, Hiroyuki Takeya, Takahide Yamaguchi, Hiroaki Kumakura, Yoshihiko Takano
arXiv:1303.3725 · DOI 10.1088/0953-2048/26/8/085023 · 2013-03-15 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The Phase diagram of SmFeAsO1-xFx in terms of x is exhibited in this study. SmFeAsO1-xFx from x = 0 to x = 0.3 were prepared by low temperature sintering with slow cooling. The low temperature sintering suppresses the formation of the amorphous FeAs, which is inevitably produced as an impurity by using high temperature sintering. Moreover, slow cooling is effective to obtain the high fluorine concentration. The compositional change from feedstock composition is quite small after this synthesis. We can reproducibly observe a record superconducting transition for an iron based superconductor at 58.1 K. This achievement of a high superconducting transition is due to the success in a large amount of fluorine substitution. A shrinking of the a lattice parameter caused by fluorine substitution is observed and the substitutional rate of fluorine changes at x =0.16.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| SmFeAsO1-xFx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 58.1 | Pressure not reported | unknown |
Similar papers
Transition Temperature and Upper Critical Field in SmFeAsO1-xFx Synthesized at Low Heating Temperatures
similarity 0.93S. J. Singh et al. · 2013 · arXiv:1303.4163
Source status unknown — claims are unverified
Antimony Doping Effect on the Superconducting Properties of SmFeAs(O,F)
similarity 0.90Azam, Mohammad et al. · 2023 · arXiv:2311.13908
Source status unknown — claims are unverified
Phase diagram of the PrFeAsOF superconductor
similarity 0.90C. R. Rotundu et al. · 2009 · arXiv:0907.1308
Source status unknown — claims are unverified
Superconductivity at 41.0 K in the F-doped LaFeAsO1-xFx
similarity 0.90Wei Lu et al. · 2008 · arXiv:0804.3725
Source status unknown — claims are unverified
Superconductivity induced by U doping in the SmFeAsO system
similarity 0.89Bo Huang et al.
Source status unknown — claims are unverified
Synthesis and Microstructural Studies of Iron Based LaO1-xFxFeAs Superconducting Materials
similarity 0.89Chandra Shekhar et al. · 2008 · arXiv:0806.1661
Source status unknown — claims are unverified