Growth of superconducting Sm(O,F)BiS2 single crystals

Koki Kinami; Yuji Hanada; Masanori Nagao; Akira Miura; Yosuke Goto; Yuki Maruyama; Satoshi Watauchi; Yoshihiko Takano; Isao Tanaka

doi:10.1021/acs.cgd.9b00451

Growth of superconducting Sm(O,F)BiS2 single crystals

Koki Kinami, Yuji Hanada, Masanori Nagao, Akira Miura, Yosuke Goto, Yuki Maruyama, Satoshi Watauchi, Yoshihiko Takano, Isao Tanaka

arXiv:1911.02337 · DOI 10.1021/acs.cgd.9b00451 · 2019-11-06 · Crystal Growth & Design

T1experimental7 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Superconducting Sm(O,F)BiS2 single crystals were successfully grown using KI-KCl flux. The obtained single crystals were flat-shaped and their size was 500um. The structure and composition of the obtained single crystals were obtained using X-ray diffraction and X-ray spectroscopy. The lattice constants of the obtained Sm(O,F)BiS2 single crystals were evaluated to be a = 3.9672(4) A and c = 13.417(6) A, while their F/(O + F) molar ratio was approximately 0.17. The superconducting transition temperature of the obtained Sm(O,F)BiS2 single crystals was 4.8 K. This was different from the reported Sm(O,F)BiS2 with no superconducting transition above 2 K. The superconducting anisotropies of the upper critical field and effective mass model of the obtained Sm(O,F)BiS2 single crystals were estimated to be approximately 26 and 10, respectively.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Sm(O,F)BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.8	Pressure not reported	unknown