Crystal structure and phase transitions at high pressures in the superconductor FeSe0.89S0.11
Yulia A. Nikiforova, Anna G. Ivanova, Kirill V. Frolov, Igor S. Lyubutin, Dmitriy A. Chareev, Arseniy O. Baskakov, Sergey S. Starchikov, Ivan A. Troyan, Mariana V. Lyubutina, Pavel G. Naumov, Mahmoud Abdel-Hafiez
arXiv:2009.11223 · DOI 10.1016/J.JALLCOM.2020.158419 · 2020-09-23 · Journal of Alloys and Compounds
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report on the structural phase transitions in the S doped FeSe superconductor by powder synchrotron X ray diffraction at high pressures up to 18.5 GPa under compression and decompression modes. In order to create high quasi hydrostatic pressures, diamond anvil cells filled with helium as a pressure transmitting medium were used. It was found that at ambient pressure and room temperature, S doped FeSe has a tetragonal structure. Under compression, in the region of 10 GPa, a phase transition from the tetragonal into the orthorhombic structure is observed, which persists up to 18.5 GPa. Our results strongly suggest that, at decompression, as the applied pressure decreases to 6 GPa and then is completely removed, most of the sample recrystallizes into the hexagonal phase of the structural type NiAs. However, the other part of the sample remains in the high pressure orthorhombic phase, while the tetragonal phase is not restored. These observations illustrate a strong hysteresis of the structural properties of S doped FeSe during a phase transition under pressure.
Similar papers
Simultaneous measurement of pressure evolution of crystal structure and superconductivity in FeSe0.92 using designer diamonds
similarity 0.92Uhoya, Walter et al. · 2012 · arXiv:1210.3645
Source status unknown — claims are unverified
Structural and optical investigations of the iron-chalcogenide superconductor FeSeTe under high pressure
similarity 0.91Pallavi S. Malavi et al. · 2013 · arXiv:1308.3367
Source status unknown — claims are unverified
High temperature superconductivity (Tc onset at 34K) in the high pressure orthorhombic phase of FeSe
similarity 0.90G. Garbarino et al. · 2009 · arXiv:0903.3888
Source status unknown — claims are unverified
Enhanced Superconductivity on the Tetragonal Lattice in FeSe under Hydrostatic Pressure
similarity 0.90Kiyotaka Miyoshi et al. · 2013 · arXiv:1310.7546
Source status unknown — claims are unverified
Why Does Undoped FeSe Become a High-Tc Superconductor under Pressure?
similarity 0.89T. Imai et al.
Source status unknown — claims are unverified
Pressure Induced Static Magnetic Order in Superconducting FeSe1−x
similarity 0.89M. Bendele et al.
Source status unknown — claims are unverified