High-performance Ba1-xKxFe2As2 superconducting joints for persistent current operation
Yanchang Zhu, Dongliang Wang, Qiqi Wang, Wenwen Guo, Cong Liu, He Huang, Hongjun Ma, Fang Liu, Huajun Liu, Yanwei Ma
arXiv:2109.14300 · DOI 10.1088/1361-6668/ac4ff1 · 2021-09-29 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconducting joints are one of the key technologies to make Ba1-xKxFe2As2 (Ba-122) superconducting wires or tapes for high-field applications. Herein, superconducting joints were fabricated by a simple cold-pressing method, and the joint resistance of the iron-based superconducting joint was estimated for the first time. The superconducting properties, microstructures, and elements distribution in the joint regions were investigated. At 4.2 K and 10 T, a transport critical current Ic of 105 A for the joint was obtained, and the critical current ratio (CCR= Ic-joint/Ic-tape) of the joint was 94.6%. On the other hand, the joint show very low joint resistance of 2.7x10^-13 ohm in self-field at 4.2 K. Among iron-based superconductors (IBS), this work is the first to successfully realize a superconducting joint with such high CCR and low joint resistance. This work shows great potential to apply Ba-122 in a range of practical applications, where superconducting joints are essential.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Ba1-xKxFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
| Ba1-xKxFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Superconducting joint between iron-based superconductor tapes
similarity 0.93Yanchang Zhu et al. · 2018 · arXiv:1805.03399
Source status unknown — claims are unverified
High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process
similarity 0.88Zhaoshun Gao et al. · 2014 · arXiv:1412.1580
Source status unknown — claims are unverified
High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks
similarity 0.87J. D. Weiss et al. · 2012 · arXiv:1204.4426
Source status unknown — claims are unverified
Improved transport critical currents in Ag and Pb co-doped BaxK1-xFe2As2 superconducting tapes
similarity 0.87Chao Yao et al. · 2012 · arXiv:1202.1039
Source status unknown — claims are unverified
Mechanochemical synthesis of pnictide compounds and superconducting Ba0.6K0.4Fe2As2 bulks with high critical current density
similarity 0.86J. D. Weiss et al. · 2013 · arXiv:1305.6820
Source status unknown — claims are unverified
Enhanced high-field transport critical current densities observed for the ex-situ PIT processed Ag/(Ba,K)Fe2As2 thin tapes
similarity 0.86K. Togano et al. · 2013 · arXiv:1302.0482
Source status unknown — claims are unverified