Phase purity and surface morphology of high-Jc superconducting Bi2Sr2Ca1Cu2O8+δ thin films
Keppert, Sandra, Aichner, Bernd, Adhikari, Rajdeep, Faina, Bogdan, Lang, Wolfgang, Pedarnig, Johannes D.
arXiv:2306.14481 · DOI 10.1016/j.apsusc.2023.157822 · 2023-06-27
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Bi2Sr2Ca1Cu2O8+d (Bi-2212) thin films with thicknesses less than 50 nm (<20 unit cells) are grown by pulsed laser deposition (PLD) onto (001) LaAlO3 (LAO) single crystal substrates. Phase-pure and smooth c-axis oriented Bi-2212 films with optimal oxygen doping, critical temperature Tc0 up to 86 K, and critical current density Jc(60 K) above 1 MA/cm2 are obtained for samples that are annealed in situ at temperatures below 700 °C. At higher temperature Bi-2212 films on LAO substrates partially decompose to non-superconducting impurity phases, while films on MgO and SrTiO3 substrates are stable. The broadening of Tc of the metal-to-superconductor resistive phase transition in magnetic fields is much larger for thin films of Bi-2212 as compared to YBa2Cu3O7. The magnetic field-induced suppression of Tc0 is stronger for Bi-2212 films containing impurity phases as compared to the phase-pure Bi-2212 films. The degradation of LAO substrate crystals after several steps of deposition and chemical removal of the Bi-2212 layer is investigated. New, commercially prepared substrates provide Bi-2212 films with smallest surface roughness (3 nm) and strong out-of-plane texture. However, thin films of almost the same quality are obtained on re-used LAO substrates that are mechanically polished after the chemical etching.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Bi2Sr2CaCu2O8+δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 86 | Pressure not reported | zero_resistance |
Similar papers
Enhanced superconducting properties of BiSrCaCuO films with sub-50-nm thickness
similarity 0.91Bernd Aichner et al. · 2024 · arXiv:2412.17367
Source status unknown — claims are unverified
Doping dependence of the critical current in Bi2Sr2CaCu2Oy
similarity 0.90Muntaser Naamneh et al. · 2014 · arXiv:1411.6393
Source status unknown — claims are unverified
Effect of La-doping on growth and superconductivity of Bi-2212 crystals
similarity 0.87H. Jin & J. Kötzler · 1999 · arXiv:cond-mat/9909077
Source status unknown — claims are unverified
Scaling behaviour of the critical current in clean epitaxial Ba(Fe1-xCox)2As2 thin films
similarity 0.87Iida, K. et al. · 2010 · arXiv:1001.2505
Source status unknown — claims are unverified
Enhanced critical-current in P-doped BaFe2As2 thin films on metal substrates arising from poorly aligned grain boundaries
similarity 0.87Hikaru Sato et al. · 2016 · arXiv:1606.01477
Source status unknown — claims are unverified
Interplay of doping and structural modulation in superconducting Bi2Sr2−xLaxCuO6+δ thin films
similarity 0.87Z. Z. Li et al.
Source status unknown — claims are unverified