Degradation of superconducting properties in MgB2 films by exposure to water
H Y Zhai, H M Christen, L Zhang, M Paranthaman, P H Fleming, D H Lowndes
arXiv:cond-mat/0104309 · DOI 10.1088/0953-2048/14/7/301 · 2001-04-17 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The effect of water exposure on MgB2 is studied by submerging an 800 nm thick MgB2 film into deionized water at room temperature for 1 hour, 4 hours, 10 hours, and 15 hours, and by analyzing the resulting material using scanning electron microscopy and resistance vs. temperature measurements. It is clearly observed that Tconset of these films (obtained by an ex-situ reaction of a e-beam evaporated boron layer) remains unchanged throughout this process, indicating that at least a portion of the sample retains its original bulk-like properties. The data is consistent with an interpretation in which a portion of the exposed film - likely the region closest to the substrate - becomes superconducting only at about 25 K. It is possible that this low-Tc region already exists in the as-prepared film, and we observe that its Tc coincides with that of MgB2 films obtained by annealing precursor films prepared by pulsed laser deposition. Therefore the data presented here not only illustrate the degradation of MgB2 in water but also shed light onto the differences and similarities between films obtained via different routes.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 25 | Pressure not reported | onset |
Similar papers
Influence of Mg Deficiency on the Superconductivity in MgB2 Thin Films Grown by using HPCVD
similarity 0.89Ji Young Huh et al. · 2007 · arXiv:0709.1989
Source status unknown — claims are unverified
Growth mechanism of superconducting MgB2 films prepared by various methods
similarity 0.88H. Y. Zhai et al. · 2001 · arXiv:cond-mat/0103618
Source status unknown — claims are unverified
Study of the microwave electrodynamic response of MgB2 thin films
similarity 0.88A. Andreone et al. · 2001 · arXiv:cond-mat/0109465
Source status unknown — claims are unverified
Low Temperature Fabrication of MgB2
similarity 0.88N. Rogado et al. · 2001 · arXiv:cond-mat/0107534
Source status unknown — claims are unverified
Superconducting properties of MgB2 thin films prepared on flexible plastic substrates
similarity 0.88P. Kus et al. · 2002 · arXiv:cond-mat/0206442
Source status unknown — claims are unverified
In-situ growth of superconducting MgB2 thin films by molecular beam epitaxy
similarity 0.87K Ueda & M. Naito · 2002 · arXiv:cond-mat/0210259
Source status unknown — claims are unverified