Fast formation and superconductivity of MgB2 thick films grown on stainless steel substrate
A. H. Li, X. L. Wang, M. Ionescu, S. Soltonian, J. Horvat, T. Silver, H. K. Liu, S. X. Dou
arXiv:cond-mat/0104501 · DOI 10.1016/S0921-4534(01)00886-3 · 2001-04-26 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by heating samples to 660 oC then immediately cooling down to room temperature. XRD shows above 90% MgB2 phase and less than 10 % MgO. However, the samples sintered at 800 oC for 4 h contain both MgB4 and MgO impurities in addition to MgB2. The fast formed MgB2 films appear to have a good grain connectivity that gives a Jc of 8 x 10 4 A/cm2at 5 K and 1 T and maintained this value at 20 K in zero field.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
MgB2 thick film grown on Stainless steel substrate with ductility
similarity 0.92Qing-rong Feng et al. · 2004 · arXiv:cond-mat/0408597
Source status unknown — claims are unverified
Low Temperature Fabrication of MgB2
similarity 0.90N. Rogado et al. · 2001 · arXiv:cond-mat/0107534
Source status unknown — claims are unverified
Electrical and structural properties of MgB2 films prepared by sequential deposition of B and Mg on the NbN buffered Si(100) substrate
similarity 0.90S. Chromik et al. · 2004 · arXiv:cond-mat/0401569
Source status unknown — claims are unverified
MgB2 superconductor thin films on Si and Al2O3 substrates
similarity 0.90A. Plecenik et al. · 2001 · arXiv:cond-mat/0105612
Source status unknown — claims are unverified
Superconducting properties of MgB2 thin films prepared on flexible plastic substrates
similarity 0.90P. Kus et al. · 2002 · arXiv:cond-mat/0206442
Source status unknown — claims are unverified
Growth and Properties of Superconducting MgB2 Thin Films
similarity 0.89Michio Naito & Kenji Ueda · 2004 · arXiv:cond-mat/0402333
Source status unknown — claims are unverified