Very fast formation of superconducting MgB2/Fe wires with high Jc
X. L. Wang, S. Soltanian, J. Horvat, M. J. Qin, H. K. Liu, S. X. Dou
arXiv:cond-mat/0106148 · DOI 10.1016/S0921-4534(01)00900-5 · 2001-06-08 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
In this paper we have investigated the effects of sintering time and temperature on the formation and critical current densities of Fe-clad MgB2 wires. MgB2 wires were fabricated using the powder-in-tube process and sintered for different periods of time at predetermined temperatures. All the samples were examined using XRD, SEM and magnetisation measurements. In contrast to the common practice of sintering for several hours, the present results show that there is no need for prolonged heat treatment in the fabrication of Fe-clad MgB2 wires. A total time in the furnace of several minutes is more than enough to form nearly pure MgB2 with high performance characteristics. The results from Tc, Jc and Hirr show convincingly that the samples which were sintered for 3 minutes above 800 oC are as good as those sintered for longer times. In fact, the Jc field performance for the most rapidly sintered sample is slightly better than for all other samples. Jc of 4.5 times 10 ^5 A/cm2 in zero field and above 10 ^5 A/cm2 in 2T at 15 K has been achieved for the best Fe-clad MgB2 wires. As a result of such a short sintering there is no need for using high purity argon protection and it is possible to carry out the heat treatment in a much less protective atmosphere or in air. These findings substantially simplify the fabrication process, making it possible to have a continuous process for fabrication and reducing the costs for large-scale production of MgB2 wires.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Improvement of critical current density in the Cu/MgB2 and Ag/MgB2 superconducting wires using the fast formation method
similarity 0.94S. Soltanian et al. · 2002 · arXiv:cond-mat/0201261
Source status unknown — claims are unverified
Influence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires
similarity 0.89Y. F. Wu et al. · 2006 · arXiv:cond-mat/0607223
Source status unknown — claims are unverified
Fabrication of high performance MgB2 wires by an internal Mg diffusion process
similarity 0.88J. M. Hur et al. · 2007 · arXiv:0712.2273
Source status unknown — claims are unverified
Effects of carbon concentration and filament number on advanced internal-Mg-infiltration-processed MgB2 Strands
similarity 0.87G Z Li et al. · 2013 · arXiv:1307.1150
Source status unknown — claims are unverified
High performance new MgB2 superconducting hollow wires
similarity 0.87G. Giunchi et al. · 2002 · arXiv:cond-mat/0207488
Source status unknown — claims are unverified
Properties of superconducting MgB_2 wires: "in-situ" versus "ex-situ" reaction technique
similarity 0.87Alexey V Pan et al. · 2003 · arXiv:cond-mat/0302249
Source status unknown — claims are unverified