Ling An, Chinping Chen, Bo Wang, Cheng-gang Zhuang, Xing-guo Li, Zeng-jun Zhou, Qing-rong Feng
arXiv:cond-mat/0410533 · 2004-10-21
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The size effect of the raw B powder on the MgB2 phase formation has been studied by the technique of in-situ high temperature resistivity (HT-rT) measurement. The onset temperature, Tonset, and the completion temperature, TPF, of the phase formation are determined directly during the ongoing thermal process. These two temperatures, Tonset and TPF of the sample synthesized using nanometer B and Mg powders (NanoB-MgB2) are 440 C and 490 C, respectively, the same as those of the sample using micrometer B and nanometer Mg powders (MicroB-MgB2). This indicates that the phase formation temperature of MgB2 do not depend on the B powder size. On the other hand, the upper limit of the sintering temperature, TN, above which the sample loses superconductivity, is below 750 C for NanoB-MgB2, much lower than 980 C for the MgB2 prepared using micron-sized B powder and millimeter sized Mg powder (DM-MgB2). In comparison with the sample directly sintered at 650 C < TN, an interesting, irreversible transformation in the crystal structure of the MgB2 phase was observed with the sample going through the stages of initial sintering at 750 C, then re-sintering at 650 C in an Mg-rich environment after the processes of regrinding and pressing. Possible explanation of the observed properties is discussed.
Similar papers
Phase formation of polycrystalline MgB2 at low temperature using nanometer Mg powder
similarity 0.95Chinping Chen et al. · 2004 · arXiv:cond-mat/0406398
Source status unknown — claims are unverified
Growth of superconducting MgB2 thin films via postannealing techniques
similarity 0.89W. N. Kang et al. · 2002 · arXiv:cond-mat/0209226
Source status unknown — claims are unverified
The Influence of Synthesis Parameters on Microstructures and Superconducting Properties of MgB2 Bulks
similarity 0.89Y. F. Wu et al. · 2006 · arXiv:cond-mat/0603536
Source status unknown — claims are unverified
Temperature- and magnetic-field-dependent resistivity of MgB2 sintered at high temperature and high pressure condition
similarity 0.88C. U. Jung et al. · 2001 · arXiv:cond-mat/0102215
Source status unknown — claims are unverified
The effect of inhomogeneous phase on the critical temperature of smart meta-superconductor MgB2
similarity 0.87Honggang Chen et al. · 2017 · arXiv:1712.00245
Source status unknown — claims are unverified
Effects of Ion Milling on the Microwave Properties of MgB2 Films
similarity 0.87Sang Young Lee et al. · 2002 · arXiv:cond-mat/0208304
Source status unknown — claims are unverified