Phase formation of polycrystalline MgB2 at low temperature using nanometer Mg powder
Chinping Chen, Zeng-jun Zhou, Xing-guo Li, Jun Xu, Yu-hao Wang, Yong-zhong Wang, Qing-rong Feng
arXiv:cond-mat/0406398 · DOI 10.1016/j.ssc.2004.03.058 · 2004-06-17 · Solid State Communications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The MgB2 superconductor synthesized in a flowing argon atmosphere using nanometer magnesium powder as the raw materials, denoted as Nano-MgB2, has been studied by the technique of in-situ high temperature resistance measurement (HT-RT measurement). The MgB2 phase is identified to form within the temperature range of 430 to 490 C, which is much lower than that with the MgB2 sample fabricated in the same gas environment using the micron-sized magnesium powder, denoted as Micro-MgB2, reported previously. The sample density of the Nano-MgB2 reaches 1.7 g/cm3 with a crystal porosity structure less than a micrometer, as determined by the scanning electron microscope (SEM) images, while the Micro-MgB2 has a much more porous structure with corresponding density of 1.0 g/cm3. This indicates that the Mg raw particle size, besides the sintering temperature, is a crucial factor for the formation of high density MgB2 sample, even at the temperature much lower than that of the Mg melting, 650 C. The X-ray diffraction (XRD) pattern shows a good MgB2 phase with small amount of MgO and Mg and the transition temperature, TC, of the Nano-MgB2 was determined as 39 K by the temperature dependent magnetization measurement (M-T), indicating the existence of a good superconducting property.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 39 | Pressure not reported | unknown |
Similar papers
Effect of nanometer-sized B powder on phase formation of polycrystalline MgB2
similarity 0.95Ling An et al. · 2004 · arXiv:cond-mat/0410533
Source status unknown — claims are unverified
The Influence of Synthesis Parameters on Microstructures and Superconducting Properties of MgB2 Bulks
similarity 0.91Y. F. Wu et al. · 2006 · arXiv:cond-mat/0603536
Source status unknown — claims are unverified
Low Temperature Fabrication of MgB2
similarity 0.90N. Rogado et al. · 2001 · arXiv:cond-mat/0107534
Source status unknown — claims are unverified
Superconducting Properties of Combustion Synthesized MgB2
similarity 0.90Takano, Yoshihiko et al. · 2016 · arXiv:cond-mat/0401572
Source status unknown — claims are unverified
Effect of sintering temperature under high pressure in the uperconductivity for MgB2
similarity 0.90C. U. Jung et al. · 2001 · arXiv:cond-mat/0102383
Source status unknown — claims are unverified
Improved Superconducting Properties in Bulk MgB2 Prepared by High Energy Milling of Mg and B Powder
similarity 0.89Wu, Y. F. et al. · 2008 · arXiv:cond-mat/0607318
Source status unknown — claims are unverified