Superconductivity in porous MgB2
V. A. Grinenko, E. P. Krasnoperov, V. A. Stoliarov, A. A. Bush, B. P. Mikhajlov
arXiv:cond-mat/0503614 · DOI 10.1016/j.ssc.2006.03.036 · 2005-03-25
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Porous magnesium diboride samples have been prepared by the heat treatment of a pressed mixture of Mg and MgB2 powders. It was found that linked superconducting structure is formed down to the minimum normalized density gamma= d/do= 0.16 (percolation threshold), where d is the density of MgB2 averaged over the sample, do= 2.62 g/cm3 is the X-ray density. Lattice parameters and critical temperature of the porous sample decrease with increasing porosity (decreasing gamma) and Tc2= 32K is minimal at gamma= 0.16. The grain boundaries in the porous samples are transparent for the current and Jc~3.105A/cm2 in self field at T= 20K in the samples with gamma~ 0.24.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 32 | Pressure not reported | unknown |
Similar papers
Superconducting Properties of MgB2 Bulk Materials Prepared by High Pressure Sintering
similarity 0.90Y. Takano et al. · 2001 · arXiv:cond-mat/0102167
Source status unknown — claims are unverified
Connectivity and Critical Currents in Polycrystalline MgB2
similarity 0.90M. Eisterer et al. · 2008 · arXiv:0811.0986
Source status unknown — claims are unverified
High critical current densities in superconducting MgB2 thin films
similarity 0.88S. H. Moon et al. · 2001 · arXiv:cond-mat/0104230
Source status unknown — claims are unverified
Temperature- and magnetic-field-dependent resistivity of MgB2 sintered at high temperature and high pressure condition
similarity 0.88C. U. Jung et al. · 2001 · arXiv:cond-mat/0102215
Source status unknown — claims are unverified
Phase formation of polycrystalline MgB2 at low temperature using nanometer Mg powder
similarity 0.88Chinping Chen et al. · 2004 · arXiv:cond-mat/0406398
Source status unknown — claims are unverified
Superconductivity in Dense Wires
similarity 0.88P. C. Canfield et al. · 2001 · arXiv:cond-mat/0102289
Source status unknown — claims are unverified