Si doping on MgB2 thin films by pulsed laser deposition
Y. Zhao, M. Ionescu, J. Horvat, A. H. Li, S. X. Dou
arXiv:cond-mat/0311055 · 2003-11-04 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A series of MgB2 thin films were fabricated by pulsed laser deposition (PLD), doped with various amounts of Si up to a level of 18wt%. Si was introduced into the PLD MgB2 films by sequential ablation of a stoichiometric MgB2 target and a Si target. The doped films were deposited at 250 C and annealed in situ at 685 C for 1min. Up to a Si doping level of ~11wt%, the superconducting transition temperature (Tc) of the film does not change significantly, as compared to the control, undoped film. The magnetic critical current density (Jc) of the film at 5K was increased by 50% for a Si doping level of ~3.5wt%, as compared to the control film. Also, the irreversibility field of Si-doped MgB2 films (Hirr) at low temperature is higher than for the undoped film.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Superconducting thin films of MgB2 on (001)-Si by pulsed laser deposition
similarity 0.92A. Brinkman et al. · 2001 · arXiv:cond-mat/0103198
Source status unknown — claims are unverified
Superconducting magnesium diboride films on Silicon with Tc0 about 24K grown via vacuum annealing from stoichiometric precursors
similarity 0.90H. Y. Zhai et al. · 2001 · arXiv:cond-mat/0103588
Source status unknown — claims are unverified
Effect of SiC-Impurity Layer and Growth Temperature on MgB2 Superconducting Tapes Fabricated by HPCVD
similarity 0.90Mahipal Ranot et al. · 2011 · arXiv:1112.1908
Source status unknown — claims are unverified
In-situ Magnesium Diboride Superconducting Thin Films grown by Pulsed Laser Deposition
similarity 0.89G. Grassano et al. · 2001 · arXiv:cond-mat/0103572
Source status unknown — claims are unverified
Superconducting Mg-B films by pulsed laser deposition in an in-situ two-step process using multi-component targets
similarity 0.89D. H. A. Blank et al. · 2001 · arXiv:cond-mat/0103543
Source status unknown — claims are unverified
Thickness dependence of the properties of epitaxial MgB2 thin films grown by hybrid physical-chemical vapor deposition
similarity 0.88A. V. Pogrebnyakov et al. · 2003 · arXiv:cond-mat/0304164
Source status unknown — claims are unverified